Low Stainless Steel Welding Rods
E308L-16
Description:
It is a super low carbon stainless steel electrode with titanium calcium coating. It can be used for both alternating and direct current. Due to low sugar content, it can resist intercrystalline corrosion caused by carbide precipitation when there is no stabilizer such as niobium and titanium.
USES:
Deposited Metal Chemical Composition :
C | Mn | Si | Cr | Ni | Mo | S | P | Cu | |
Standard | ≤0.04 | 0.5-2.5 | ≤0.90 | 22.0-25.0 | 12.0-14.0 | ≤0.75 | ≤0.030 | ≤0.040 | ≤0.75 |
Test | 0027 | 0.85 | 0.67 | 24.2 | 13.09 | 0.09 | 0.009 | 0.020 | 0.092 |
Deposited Metal Mechanical Performance:
Tensile Strength Rm (MPa) | Enlength A (%) | |
Standard | ≥520 | ≥25 |
Test | 565 | 41 |
Referential Current (DC or AC)
Diameter (MM) | 2.5 | 3.2 | 4.0 | 5.0 |
Length (MM) | 350 | 350 | 400 | 400 |
Current (A) | 50-70 | 80-110 | 130-160 | 160-200 |