A002 is a super-low carbon Cr19Ni10 stainless steel type electrode coated with Titanium-calcium.The molten content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performace on both AC and DC.
It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainess steel 0Cr19NillT1 which working temperature below 300ºC.It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.
|Chemical Composition Deposited Metal (%)|
|Mechanical Properties of Deposited metal|
|Test Item||Tensile Strength|
|Sizes & Recommended Current (AC or DC)|
|Welding rod diameter (mm)||2.0||2.5||3.2||4.0||5.0|
|welding current (A)||25~50||50~80||80~110||110~160||160~200|
1.Electrodes must be baked for 1 hour at 150ºC before welding operation.
2.To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3.The anti-corrosion performance and ferrite composition should be detemined between buyer and seller.