Lincoln 860, OK FLUX 10.82 Welding Flux SJ301
1.Specifications:
AWS-A5.17 F6A0-EL8 F7A2-EM12K EN760 SA CS 1 89 AC H5
2.Description:
SJ301 is an agglomerated calcium-silicate type welding flux. Basicity: 1. 0 (B//W) It is gray and round grain,mesh:10-40.Regularly shaped welds are deposited without reduction of area or interface notches. Slag detachability is good. A short slag is produced, thus allowing circumferential welding on small-diameter workpieces without the risk of uncontrolled slag. The production of large pipes(especially spiral pipe welding) is a typical application for this flux. Relatively high manganese pick-up is obtained,thus allowing the flux to be used with wires with a low Mn content.
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.
Applications:
The flux is fit for the submerge-arc welding of low-carbon steel and low-alloy steel. Butt and flat fillet welding of miniature LPG tanks pipeline steel,,ships,vehicles,agricultural implements,machinery,boilers,bridges,structural steels.
Chemical Composition(%)
| SiO2+TiO2 | Al2O3+MnO | CaO+MgO | CaF2 | S | P |
| 25-35 | 30-40 | 15-25 | 5-15 | ≤0.05 | ≤0.05 |
Mechanical Performance of the Deposited Metal
Wires | Standard Models | Yield Point Rel(MPa) | Tensile Strength Rm(MPa) | Elongation A (%) | Impact Value Kv2(J) |
| EL8 EM12K | F6A0-EL8 F7A2-EM12K | ≥350 ≥410 | 415-550 480-650 | ≥22 ≥30 | ≥40(0ºC) ≥60(-20ºC) |
Attention:
1. We get values in data sheets from tests carried out in accordance to AWS and GB standard procedure. They only represent values we get under those conditions. They are not to be taken as guarantees. AS to welding ,individual test results may depending on experience & technique, flux type, base metal, joint preparation, flux preparation, ampere, voltage, etc.
2. If welding fluxes are stored in improper environment or influenced by condensed moisture, anyway, they get damp, please dry them at 300-350 for 2 hours before usage.
3. Please clean the rust,oil,water on base metal before welding.
4. Add minimum 20% new flux when using recovered flux to avoid welding defects and maintain welding performance & mechanical properties.
5. Please control parameters properly, like preheat temperature, interpass temperature,cooling rate.
Company Brief Introduction
(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact us: