High quality Submerged arc Welding Flux SJ101 & SAW Wire EM12K best matching for bridge building
Submerged arc welding flux SJ101 technical specification:
Specifications:
AWS A5.17/5.23 F6A0-EL8 F6A2-EM12 F7A2-EM12K F7A4-EH14
EN760 SA FB 1 65 AC H5
Description:
SJ101 is an agglomerated fluoride-basic type flux. It is gray and round grain,mesh 10-60. it can be operated with AC and DC. ,the welding electric current can up to 1200A.It has excellent weldability, the welding bead appearance is beautiful and the slag is easy to remove. The diffusible hydrogen content in deposited metal is less than 5ml/100g,so it has very good toughness at low temperature,therefore,crack resistance is extremely high. It is suitable for submerged arc twin-wire,tandom and multi-wire welding as well as for welding with the two-run technique.
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.
Usage:
It can be applied to different welding wires(such as H08MnA,H10mN2,H10MnSi,H08Mn2MoA,H08Mn2SiA etc.) It is fit for welding of low-carbon steel and low alloy steel. Such as oil storage tanks,pipeline steel,ships,bridges,pressure vessels,penstocks,boilers and H-beam structural steels.
Chemical Composition(%)
Mechanical Performance of the Deposited Metal
Our service
1)Prime quality+Competitive price+Thoughtful Service=100% Satisfication
2)We can research and produce customerized fluxes according to your different demands.
3)SAW Welding Flux Expert- One Stop Solution For Submerged Arc Welding consumables.
Submerged arc welding wire EM12/EL8/EH14 technical specification:
Products Picture:
Company Brief Introduction
(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact us:
Submerged arc welding flux SJ101 technical specification:
Specifications:
AWS A5.17/5.23 F6A0-EL8 F6A2-EM12 F7A2-EM12K F7A4-EH14
EN760 SA FB 1 65 AC H5
Description:
SJ101 is an agglomerated fluoride-basic type flux. It is gray and round grain,mesh 10-60. it can be operated with AC and DC. ,the welding electric current can up to 1200A.It has excellent weldability, the welding bead appearance is beautiful and the slag is easy to remove. The diffusible hydrogen content in deposited metal is less than 5ml/100g,so it has very good toughness at low temperature,therefore,crack resistance is extremely high. It is suitable for submerged arc twin-wire,tandom and multi-wire welding as well as for welding with the two-run technique.
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.
Usage:
It can be applied to different welding wires(such as H08MnA,H10mN2,H10MnSi,H08Mn2MoA,H08Mn2SiA etc.) It is fit for welding of low-carbon steel and low alloy steel. Such as oil storage tanks,pipeline steel,ships,bridges,pressure vessels,penstocks,boilers and H-beam structural steels.
Chemical Composition(%)
| SiO2+TiO2 | Al2O3+MnO | CaO+MgO | CaF2 | S | P |
| 15-25 | 20-30 | 25-35 | 25 | ≤0.06 | ≤0.08 |
Mechanical Performance of the Deposited Metal
| WIRE | Yield Point Rel(MPa) | Tensile Strength Rm(MPa) | Elongation A (%) | Charpy V Notch Impact Strength KV2(J) | |
| -20ºC | -40ºC | ||||
| EM12 | ≥400 | 465-550 | ≥22 | ≥37 | |
| EM12K | ≥400 | 490-600 | ≥22 | ≥50 | |
| EH14 | ≥400 | 500-650 | ≥22 | ≥70 | ≥50 |
Our service
1)Prime quality+Competitive price+Thoughtful Service=100% Satisfication
2)We can research and produce customerized fluxes according to your different demands.
3)SAW Welding Flux Expert- One Stop Solution For Submerged Arc Welding consumables.
Submerged arc welding wire EM12/EL8/EH14 technical specification:
| Submerged Arc Welding Wire | |||
| Type | GB Code | AWS Code | Description |
| H08A | H08A | EL8 | Low manganese low silicon welding wire matches with high manganese and silicon welding flux,not sensitive to the rust on the base metal;has good welding shaping and slag removal performance;it is the most frequently used submerged arc welding wire,can be used in single and double pole,AC and DC welding.Cooperated with melting-type welding flux HJ431 or sintered welding flux SJ301 and SJ501,suitable for the high-speed welding of 420Mpa class base metal,and filling welding of 450Mpa carbon steel and low alloy steel. |
| H08MnA | H08MnA | EM12 | Medium manganese medium silicon welding wire matches with medium manganese and silicon welding flux,not sensitive to the rust on the base metal;has good welding shaping and slag removal performance;it can be used in single and double pole,AC and DC welding.Cooperated with melting-type welding flux HJ350 or sintered welding flux SJ301,suitable for the high-speed welding of 420Mpa class base metal and filing welding.It is used for the corresponding strengthen level of low-alloy steel welding of ships,chemistry,bridges and steel structure. |
| H10MN | H10MN | EH14 | Welding line metal with good mechanical properties can be obtained by cooperating with the corresponding welding flux(e.g.HJ230 and HJ350),used for the submerged arc automated welding of carbon steel and low alloy steel such as15Mn and 14MnNb;cooperated with the sintered welding flux SJ101,suitable for the high-speed welding of 42Mpa class base metal and filling welding.It is used for engineering welding such as ships. |
| Wire For Submerged Arc Welding | ||||||||
| Chemical Composition(%) | ||||||||
| C | Mn | Si | P | S | Cu | Ni | Cr | |
| EL8 | ≤0.10 | 0.30~0.60 | ≤0.030 | ≤0.030 | ≤0.030 | ≤0.20 | ≤0.30 | ≤0.20 |
| EM12 | ≤0.10 | 0.80~1.10 | ≤0.070 | ≤0.030 | ≤0.030 | ≤0.20 | ≤0.30 | ≤0.20 |
| EH14 | ≤0.12 | 1.50~1.90 | ≤0.070 | ≤0.035 | ≤0.035 | ≤0.20 | ≤0.30 | ≤0.20 |
| Wire For Submerged Arc Welding | |||||
| Mechanical Properties | |||||
| Tensile Strength | Yield Strength | Elongation | Test Temperature | Absorbed Energy | |
| EL8 | 415~550 | ≥330 | ≥22 | -20ºC | ≥27 |
| EM12 | 415~550 | ≥330 | ≥22 | -20ºC | ≥27 |
| EH14 | 415~550 | ≥330 | ≥22 | -20ºC | ≥47 |
Products Picture:
Company Brief Introduction(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact us: